Material
Comparisons
| Product |
Resin Type |
Suitable
Substrate |
Lubricant
Pigment |
Temperature
Capability |
Pencil
Hardness |
Load Bearing
Capacity |
Taber
Abrasion
Resistance* |
Corrosion
Resistance |
Chemical
Resistance |
1500 series
Chemical,
Corrosion &
Abrasion
Resistant
with/without
Lubricants |
proprietary |
metals, hard
plastic, glass |
none |
500°
F. |
9H+ |
medium |
3.8 |
VG |
VG |
| PTFE |
500° F. |
7H |
medium |
|
VG |
G |
| MoS2 |
500° F. |
7H |
high |
|
VG |
G |
| Graphite |
500° F. |
7H |
medium |
|
G |
P |
| |
1600 series
Corrosion Resistant |
organic |
metals |
none |
400° F. |
4H |
N/A |
46 |
VG |
G |
| inorganic |
metals |
|
800° F. |
5H |
N/A |
|
VG |
P |
| |
1700 series
Solid Film Lubricants |
organic |
metals |
PTFE |
400° F. |
4H |
low |
110 |
G |
F |
| metals |
MoS2 |
400° F. |
H |
high |
|
G |
F |
| metals |
Graphite |
400° F. |
H |
medium |
|
P |
P |
| inorganic |
metals |
PTFE |
400° F. |
4H |
low |
|
P |
P |
| metals |
MoS2 |
400° F. |
H |
high |
|
P |
P |
| metals |
Graphite |
400° F. |
H |
medium |
|
P |
P |
| |
1900 series
Elastomeric Coatings |
organic |
elastomers |
PTFE |
300° F. |
N/A |
N/A |
|
N/A |
N/A |
| elastomers |
MoS2 |
300° F. |
N/A |
N/A |
|
N/A |
N/A |
| elastomers |
Graphite |
300° F. |
N/A |
N/A |
|
N/A |
N/A |
| * Taper Abrasion Resistance - mg. loss / 1000 cycles per
ASTM |
| |
|
|
Corrosion Resistance |
Chemical Resistance |
| |
VG |
Very Good |
1000 + hrs. NSS |
most acids,
alkalis, & solvents at ambient, some at elevated
temperatures |
| |
G |
Good |
240 hrs. NSS |
some acids, alkalis or solvents at ambient only |
| |
F |
Fair |
96 hrs. NSS |
little resistance to chemicals |
| |
P |
Poor |
unsatisfactory |
unsatisfactory |
|
|